| 张书石,高洪波,王 玄,闫 晗,闫春岭.纳米SiO2混凝土的抗压强度研究与微观分析[J].水泥工程,2021,34(1):7-10 |
| 纳米SiO2混凝土的抗压强度研究与微观分析 |
| Study and microscopic analysis on compressive strength of Nano-SiO2 concrete |
| |
| DOI： |
| 中文关键词: 正交多项式,纳米SiO2,曲线拟合 |
| 英文关键词: orthogonal polynomial,nano-SiO2,curve fitting |
| 基金项目: |
|
| 摘要点击次数: 1069 |
| 全文下载次数: 1 |
| 中文摘要: |
| 本试验研究了不同掺量纳米SiO2对混凝土力学性能的影响，并采用XRD手段对其改善机理进行了分析。试验结果表明，适量的纳米SiO2可以提高混凝土的抗压强度，并根据试验分析得出当混凝土中纳米SiO2掺量为2.5%时混凝土抗压强度达到最大。试验采用单因素设计，根据需要采用正交多项式回归，并得出拟合方程为二次时最好。 |
| 英文摘要: |
| The effects of different dosage of nano-SiO2 on the mechanical properties of concrete were studied, and the improvement mechanism was analyzed by means of XRD.The experimental results show that an appropriate amount of nano-SiO2 can improve the compressive strength of concrete. According to the experimental analysis, the compressive strength of concrete reaches the maximum when the nano-SiO2 content in concrete is 2.5%.The single factor design was adopted in the experiment, and orthogonal polynomial regression was adopted according to the needs, and it was concluded that the best fitting equation was quadratic. |
|
查看全文
查看/发表评论 下载PDF阅读器 |
| 关闭 |
|
|
|