王立旺,朱其良,李新明,向若飞.水泥窑用耐碱浇注料的性能研究[J].水泥工程,2020,33(1):11-13
水泥窑用耐碱浇注料的性能研究
Study on properties of alkali resistant castables for cement kiln
  
DOI:
中文关键词: 
英文关键词: alkali resistance, castables, cement kiln, ceramics
基金项目:
作者单位
王立旺 浙江锦诚新材料股份有限公司 
朱其良 浙江锦诚新材料股份有限公司 
李新明 浙江锦诚新材料股份有限公司 
向若飞 浙江锦诚新材料股份有限公司 
摘要点击次数: 1353
全文下载次数: 0
中文摘要:
      本研究中以建筑陶瓷为主要原料制备耐碱浇注料,重点研究了铝酸钙水泥和硅微粉对耐碱浇注料性能的影响,并对试样的显微结构进行了分析。试验结果表明:铝酸钙水泥加入量的增加有助于110 ℃,24 h处理后常温强度的提高,而在10100 ℃,3 h处理条件下,铝酸钙水泥加入量的增加会提高基质中生成的液相,加入量在一定范围内使强度出现先增加后降低的趋势,同时也导致了线变化率的增加,在试验条件下铝酸钙水泥的合适加入量在7%~8%左右;耐碱浇注料中加入活性较高的硅微粉能够提高试样的强度和致密度,其加入量增加也会导致试样线变化率的增加,综合分析硅微粉的加入量以5%~6%为宜;经1 100 ℃,3 h处理后的试样中骨料和基质结合牢固,基质中存在莫来石化和低共熔物生成的双重反应。
英文摘要:
      In this study, building ceramics were used as the main raw materials to prepare alkali resistant castables. The effect of calcium aluminate cement and microsilica on the properties of alkali resistant castables was studied, and the microstructure of the samples was analyzed. The results showed that the increase of calcium aluminate cement was helpful to the increase of the strength at room temperature after treatment at 110 ℃ for 24 hours. While at 1100 ℃ for 3 hours, the increase of calcium aluminate cement increased the formation of liquid phase in the matrix, which made the strength increase first and then decrease within a certain range, and also led to the increase of the linear rate of change.Under test conditions the appropriate amount of cement was about 7%~8%.The addition of microsilica with high activity in alkali resistant castables could improve the strength and density of the samples, and the increase of its addition would also lead to the increase of the linear change rate of the sample. According to the comprehensive analysis, it was appropriate to add 5%~6% microsilica. The aggregate and the matrix in the samples treated at 1100 ℃ for 3 hours were firmly combined, and there was a double reaction of mullitization and low eutectic mixture formation in the matrix.
查看全文   查看/发表评论  下载PDF阅读器
关闭